SISTRAL® - Our new nano-structured high performance layer
SISTRAL® – on the basis of our very successful more advanced EXXTRAL,
• for even higher requirements in case of machining, in the foreground
• for the dry high-speed processing of hardened materials (>54 HRC).
SISTRAL®, which is also anthracite colored, is characterized by a very high hardness that still protects against wear also at high temperatures, and an exceptional oxidation stability.
Cutting tasks (milling, drilling, turning, sawing, etc. ) under in-service conditions, where other layers reach the limits of thermal and mechanical loading capacity. High-performance machining (HSC) of very abrasive or hard materials (steel > 54 HRC) in dry high-speed application.
SISTRAL® is deposited in latest eifeler PVD ARC systems. With temperatures of approx. 450° C high-performance cemented carbides are mainly coated. The coating of tool steels and HSS is also possible!
|Material:||Aluminum-titanium nitride (with additives), AlTiN (nano-structured)|
|Microhardness HV 0.05:||3400 ± 500|
|Coefficient of friction against steel 100Cr6:||0,7|
|Layer Thickness [µm]:||2 – 4 |
|Maximum application temperature:||900° C / 1650° F|
|General characteristic:||Extremely high oxidation and wear resistance, high warm hardness|
|Preferred applications:||Machining under extreme conditions; high-performance cutting of very abrasive or hard materials (steel > 54 HRc); Inconel machining|
 Dependent on tool size, also for micro-tools less than 2 µm.