DUMATIC – titanium carbide - Highest levels of hardness and abrasion resistance for forming applications
This layer combines the advantages of Duplex-TiCN and FORMATIC®. The new DUMATIC layer is always manufactured as a Duplex version, therefore with a plasma diffusion process of the base material. The layer itself has a structured multi-layer design with high content of TiC (approx. 4000 HV! ). The uppermost layer is developed as slide-favorable and colored sealing coat.
Forming material-forming technology
Drawing, stamping, pressing and forming tools for the processing of high-alloy chrome/nickel materials and similar requirements. Due to the high hardness, especially suitable for cold forming and the cutting of high-strength plates and for cold forging processes with high surface pressure.
The DUMATIC layer indicates a very low tendency to cold welding with high-alloy stainless steel qualities.
As a result of the relatively low oxidation stability DUMATIC is not suitable for higher contact temperatures, as are capable of occurring e.g. with semi-warm forming technology.
|Hardness:||3.700 ± 500 HV|
|Maximum application temperature:||400°C / 750°F|
|Coefficient of friction against steel:||0,25|
|Layer thickness:||3-5 µm|